7075 tấm nhôm (AA7075 aluminium sheet) is an aluminum alloy with zinc as the primary alloying element. It has excellent mechanical properties and exhibits good ductility, cường độ cao, dẻo dai, and good resistance to fatigue. It has moderated formability when in the fully soft, annealed temper and can be heat-treated to strength levels that are comparable to many steel alloys. In fact, lớp 7075 nhôm is stronger than many types of mild steel.
7075-T6 aluminum has nearly double the strength-to-weight of grade 2 titan
các 7075 Al alloy is most preferred by the aircraft industry. The composition of this specific Al alloy is 5.1–6.1% zinc, 2.1–2.9% magnesium, 1.2–2.0% copper and less than 0.5% of silicon, sắt, mangan, titan, chromium and other trace metals
One of the key reasons to consider 7075 nhôm is for its high strength. Alloyed with zinc, it is one of the strongest alloys available and stronger than 6061. But it offers a lower level of corrosion resistance than 6061 and is also more difficult to weld. 7075 is used in marine, tự động, and aerospace applications where strength is a very high priority. It is also used in a firearms manufacturing and is even used in hang glider frames
Tấm nhôm / Plate 7075-T6/T651 is normally used for aerospace, quân đội, and automotive applications. 7075 aluminum is the strongest aluminum, with the strength of many steels, while retaining aluminum’s lightweight qualities and corrosion resistance.
| hợp kim | tâm trạng | Độ dày | Chiều rộng |
| 7075 | T651 | 4-260mm | 1200-3800mm |
| 7075 | T7651 | 4-260mm | 1200-3800mm |
| 7075 | T7351 | 4-260mm | 1200-3800mm |
Mechanical properties
| Alloy state | Direction | Độ dày (mm) | Tensile strength | Năng suất Strength | Breaking Elongation | Tiêu chuẩn |
| 7075-T651 | LT | 6-260 | 570-590Mpa | 495-515Mpa | 10-13.5 | GB/T3880 |
| 7075-T7651 | LT | 6-102 | 550-560Mpa | 480-490Mpa | 10.5-12.5 | AMS4045K |
| 7075-T7351 | LT | 6-102 | 500-520Mpa | 420-435Mpa | 10-12.5 | AMS4078 |
Nhôm 7075 is a member of the 7000 loạt, which has zinc as its main alloying component and is well known for its extraordinarily high strength. Tempering treatment can then further enhance its high mechanical strength. This property makes alloy 7075 very popular in the aerospace and defense industries.
Its strength is comparable to that of many types of steel, but it has a much lower density. The alloy is an excellent substitute to steel in high-stress applications. It also excels in withstanding fatigue stress, rendering it very reliable, a quality much sought after in the industries mentioned above.
hợp kim 7075 offers only average corrosion resistance, an outcome of the small amount of copper included in its chemical composition. It also features reasonable machinability and poor forming and weldability. Another drawback of this alloy is that it has a comparatively high-cost relative to other aluminum alloys due to its exceptionally high strength.
-
-
-