6066 T6 Aluminum Sheet is a type of 6066 アルミニウム. 6066 T6 Sheet is an aluminium alloy used in forgings and extrusion for welded structures.
ASTMB209 6066 アルミシート is furnished in the T6 temper. この気性を達成するために, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. We also know this grades as 6066-T6 Aircraft Aluminum Alloy Sheet. 6066 T6 Aluminium Sheet Temper 0, H32, H34, H38 as per ASTM B209.
| 合金 | ASTMB209 1050, 1060, 1100, 1235, 3003, 3004, 3105, 5052, 5754, 6061, 6066, 8011 |
| アルミニウム 6066 T6 Sheet Temper | ザ・, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| アルミニウム 6066 T6 Sheet Thickness | 0.5mm-150mm |
| アルミニウム 6066 T6 Sheet Width | 500-2000ミリメートル |
航空機アルミニウムシート
6066-T6 aluminum sheet has medium strength and good welding performance, which can meet the strength requirements in various application scenarios and facilitate welding processing.
ザ・ 6066 aluminum alloy is a precipitation-hardened aluminum alloy commonly used in the aerospace and transportation industries. Here are some key details about 6066 航空機アルミニウムシート:
1. Composition:
– アルミニウム (アル): 97.4-98.5%
– マグネシウム (マグネシウム): 0.8-1.2%
– シリコン (と): 0.3-0.6%
– 鉄 (鉄): 0.35% 最大
– 銅 (とともに): 0.25% 最大
– マンガン (マンガン): 0.15% 最大
2. Properties:
– High strength-to-weight ratio
– Good corrosion resistance
– Excellent formability and weldability
– Good fatigue strength
– Good thermal conductivity
3. Typical applications:
– Aircraft structures
– Marine components
– Transportation parts
– General engineering applications
4. Forms available:
– シート
– 皿
– Extrusions
– Forgings
5. Temper designations:
– 6066-T6: Solution treated and artificially aged
– 6066-T4: Solution treated and naturally aged
6. 機械的性質 (approximate for 6066-T6):
– 降伏強さ: 260 MPaで (37,700 psi)
– 抗張力: 290 MPaで (42,050 psi)
– Elongation at break: 8%
7. Surface finishes:
– Mill finish
– 磨かれた
– アルマイト
– Painted
Transportation: 6066-T6 aluminum plates are widely used in the field of transportation, such as bridges, クレーン, transport aircraft, transport ships, 等. Their lightweight and high-strength characteristics enable these devices to reduce their own weight and improve operating efficiency.
Structural engineering: In structural engineering, 6066-T6 aluminum plates are also often used as key components such as roof structures. Its strength and corrosion resistance can ensure the stability and safety of the structure.
Aerospace: Although the application of 6066-T6 aluminum plate in the aerospace field may not be as extensive as that of 2000 シリーズ 7000 series aluminum alloys, its lightweight and high-strength characteristics still make it an alternative material for some aerospace equipment.
-
-
-