kirjeldus
6005 aluminum bar or alumiiniumist varras belongs to Al-Mg series anti-rust aluminum and has good corrosion resistance, weldability and cold workability. Similar to 5182 alumiiniumist varras, but with slightly higher magnesium content and a small amount of silicon added, so the welding performance is better. It cannot be strengthened by heat treatment, but it still has good plasticity when semi-cold work hardening.
6005 aluminum bar has medium strength and high plasticity, and is especially suitable for occasions requiring high plasticity and good weldability. Its fatigue strength is high, and its plasticity decreases during cold work hardening.
6005 6005A performance lies between 6061 ja 6082, and they can be used interchangeably with 6005A. The strength and machinability of 6005-T5 are equivalent to those of 6061-T6 and superior to 6063-T6. enamgi veel, 6005 6005A exhibit better extrusion characteristics and smoother milling surfaces.
Features of 6005a 6005 alumiiniumist latt / aluminium rods
- 6005A 6005 aluminum bar or aluminium rods exhibit outstanding corrosion resistance, maintaining stable performance in various environments, especially in wet and corrosive gas conditions.
- Heat treatment can be applied to 6005 6005A, allowing for adjustments in mechanical properties and other characteristics through controlled thermal processes to meet specific application requirements.
- Notably, 6005A alloy boasts excellent extrusion performance, making it suitable for manufacturing complex-shaped components using the extrusion process.
- These 6005 alumiiniumist latt or aluminium rod offer excellent bending performance, making them suitable for applications requiring bending or shaping without excessive fracture or damage.
- They demonstrate high fatigue strength, ensuring reliability in applications involving prolonged or repeated loads.
- Mõlemad 6005 6005A alloys perform excellently in various welding methods, including gas welding, TIG welding, punktkeevitus, and roll welding, enhancing their manufacturing and processing versatility
6005a 6005 aluminum bar specifications
| sulam | 6005, 6005A |
| 6005A 6005 Aluminum Bar States | T5, T6 |
| 6005A 6005 Aluminum Bar Types | Square, Ümmargune, Hex, Flat, Wire In Black & Bright Finish |
| 6005A 6005 Extruded Aluminum Round Bar Diameter | Φ5-200mm |
| 6005A 6005 Extruded Aluminum Square Bar Diameter | 5-200mm |
| 6005A 6005 Extruded Aluminum Hexagonal Bar Diameter | 5-200mm |
| 6005A 6005 Extruded Aluminum Flat Bar Specifications | paksus:0.15-40mm Width:10-200mm |
| 6005 6005A Aluminum Cast Bar Diameter | Φ124-1350mm |
| 6005A 6005 Aluminum Bar Length | 1-6m, Random, Fix & Cut Length or as per clients’ requirement |
| 6005A 6005 Aluminum Bar Surface | Hele, Polish & must |
| 6005A 6005 Aluminum Bar Quality | free from cracks, mullid, or corrosive spots. |
| 6005A 6005 Aluminum Bar Packaging | Packaging can be tailored to other customer requirements |
| 6005A 6005 Aluminum Bar Standards | ASTM B221, EN573, EN485, ET 755-2, GB / T 3191 |
Chemical composition of 6005a 6005 alumiiniumist latt
| Element | Koosseis % | |
| 6005 | 6005A | |
| ja | 0.6-0.9 | 0.5-0.9 |
| Fe | 0.35 | 0.35 |
| koos | 0.10 | 0.3 |
| Mn | 0.10 | 0.5 |
| mg | 0.4-0.6 | 0.4-0.7 |
| Kr | 0.10 | 0.30 |
| Zn | 0.10 | 0.20 |
| Ti | 0.10 | 0.10 |
| Mn+Cr | – | 0.12-0.50 |
| Each | 0.05 | 0.05 |
| Kokku | 0.15 | 0.15 |
| al | Re | Re |
These alloys exhibit excellent bending performance and high fatigue strength. seega, they are often applied in the manufacturing of high-speed railway vehicles and subway car bodies. Using 6005A can significantly reduce the weight of vehicles and increase their operational speed.
6005 alumiiniumist latt
Physical properties of 6005a t6 6005 alumiiniumist latt
| Property | Väärtus |
| Tihedus | 2.70 g/cm³ |
| Sulamispunkt | 605℃ |
| Soojuspaisumine | 24 x10-6 /K |
| Elastsusmoodul | 70 GPa |
| Soojusjuhtivus | 188 W/m.K |
| Elektriline takistus | 0.034 x10-6 Ω.m |
- 6005 aluminum alloy contains high silicon content, lowering the melting point and improving extrusion performance. 6005A aluminum alloy contains more chromium and additional manganese to reduce stress corrosion risk and enhance toughness. The additional manganese increases extrudability and strength.
- While generally similar in overall mechanical performance, slight differences in alloy element content and processing techniques may lead to slightly different strength, plasticity, and mechanical performance under specific conditions.
- 6005 6005A alloys share similar properties with 6106 ja 6005 6005A alloys and are sometimes interchangeable. Kuid, 6005 6005A alloys exhibit superior extrusion performance, and 6005A can even replace 6061 due to its better extrudability and surface appearance.
Mechanical properties of 6005 6005a t6 alumiiniumist latt
| Mehaaniline omadus | ≤25mm | 25mm-50mm | 50mm-100mm |
| Tõestav stress | 225 Min MPa | 225 Min MPa | 215 Min MPa |
| tõmbetugevus | 270 Min MPa | 270 Min MPa | 260 Min MPa |
| Pikendus A50 mm | 8% | – | – |
| Shear Strength | 205 MPa | – | – |
| Hardness Brinell | 90 HB | 90 HB | 85HB |
| Elongation A | 10 Min % | 8 Min % | 8 Min % |
Applications of 6005A 6005 alumiiniumist latt
6005 6005A aluminum alloys belong to the Al-Mg-Si series wrought aluminum alloys, offering moderate strength, excellent plasticity, korrosioonikindlus, keevitatavus, vormitavus, and good thermal extrusion performance. Tulemusena, they have versatile applications, kaasa arvatud.
Rail transportation car body structures
6005A-T6 aluminum bar achieve medium strength through online air cooling or water mist cooling followed by artificial aging. They can be extruded into wide, flat, thin-walled hollow profiles. Sellisena, they are extensively used in the manufacturing of light rail passenger cars, raudtee sõiduautod, and especially high-speed EMU car bodies, making them indispensable materials in rail vehicle manufacturing.
High-speed EMU car fronts
6005 aluminum bar medium strength, excellent plasticity, korrosioonikindlus, keevitatavus, and formability have led to its application in welded structural components and the manufacturing of high-speed train fronts in recent years. Its exceptional overall performance makes it a key material for achieving high-speed train operations.
Building curtain walls
6005 aluminum bar sections are used as replacements for 6063 alloy sections in building curtain walls. They exhibit superior mechanical and processing properties, reducing processes and costs while meeting national standards.
Building bridges and guardrails
Aluminum guardrails made from 6005 aluminum bar are widely applied in bridge manufacturing, shops, residences, factory gates, as well as fencing at construction sites and ranches. Their lightweight nature, suur tugevus, and easy installation and disassembly characteristics provide convenience for construction.
Industrial sector
6005 alumiiniumist latt is widely used in tower structures, platvormid, structures, and pipe manufacturing. Its moderate strength, hea plastilisus, korrosioonikindlus, and formability make it an ideal material for manufacturing communication tower structures, industrial platforms, industrial ladders, and structures. It meets the requirements of outdoor and industrial environments while offering advantages in lightweight and ease of processing.
Chemical composition of aluminum alloy for extrusion
| ja | koos | mg | Zn | Fe | Mn | Ti | Kr | OTHER | TOTAL | |
| EACH | ||||||||||
| 1050 | <0.25 | <0.05 | <0.05 | <0.05 | <0.40 | <0.05 | <0.03 | <0.03 | <0.03 | <0.10 |
| 1070 | <0.20 | <0.04 | <0.03 | <0.04 | <0.25 | <0.03 | <0.03 | <0.03 | <0.03 | <0.10 |
| 2011 | <0.40 | 5.60~6.00 | <0.05 | <0.30 | <0.70 | <0.05 | <0.05 | <0.05 | Pb0.40~0.60 | Bi0.20~0.60 |
| 3003 | <0.60 | <0.05 | <0.05 | <0.10 | <0.70 | 1.00~1.50 | <0.05 | <0.05 | <0.05 | <0.15 |
| 4043 | 4.50~6.00 | <0.30 | <0.05 | <0.10 | <0.80 | <0.05 | <0.20 | <0.05 | <0.05 | <0.15 |
| 5052 | <0.25 | <0.10 | 2.20~2.80 | <0.10 | <0.40 | <0.10 | <0.05 | 0.15~0,35 | <0.05 | <0.15 |
| 5056 | <0.30 | <0.10 | 4.50~5.60 | <0.10 | <0.40 | 0.05~0.20 | <0.05 | 0.15~0.20 | <0.05 | <0.15 |
| 6005 | 0.60~0.90 | <0.10 | 0.45~0.6 | <0.10 | <0.35 | <0.10 | <0.10 | <0.10 | <0.05 | <0.15 |
| 6061 | 0.40~0.80 | 0.15~0.40 | 0.80~1.20 | <0.25 | <0.70 | <0.25 | <0.15 | 0.04~0,35 | <0.05 | <0.15 |
| 6063 | 0.20~0.60 | <0.10 | 0.45~0.90 | <0.10 | <0.35 | <0.10 | <0.10 | <0.10 | <0.05 | <0.15 |
| 7005 | <0.35 | <0.10 | 1.00~1.80 | 4.00~5.00 | <0.40 | 0.20~0.70 | 0.01~0.06 | 0.06~0.20 | Zr0.08~0.20 | <0.15 |
| 7075 | <0.40 | 1.20~2.00 | 2.10~2.90 | 5.10~6.10 | <0.50 | <0.30 | <0.20 | 0.18~0,35 | <0.05 | <0.15 |
-
-
-