5005 ایلومینیم شیٹ ایک عام ایلومینیم-میگنسیم سیریز مصر ہے (5XXX سیریز) اپنی درمیانی طاقت کے لئے جانا جاتا ہے, بہترین سنکنرن مزاحمت, اور بقایا انوڈائزنگ سطح ختم.
5005 مصر aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
RUIYI / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 ملی میٹر, as well as plates as thin as 0.2 mm with widths up to 2650 ملی میٹر, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 ایلومینیم شیٹ Introduction
| پروڈکٹ کا نام | 5005 ایلومینیم شیٹ |
| Popular Tempers | اے, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(B), A95005, 3.3315, AlMg1 |
| 5005 چادر | موٹائی: 0.008”–0.24” (0.2mm–6mm), چوڑائی: 35.4”–104” (900mm–2650mm) |
| 5005 چادر | موٹائی: 0.24”–9.84” (6mm–250mm), چوڑائی: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | موٹائی: 0.24”–9.84” (6mm–250mm), چوڑائی: 35.4”–149.6” (900mm–3800mm) |
| لمبائی | Up to 6 meters; fixed or custom-cut length available |
| Surface Finish | Mill finish, لئے Anodized, brushed, پالش, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & سفید فلم, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 ایلومینیم شیٹ
5005 Aluminum sheet with excellent formability, weldability کو, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% میگنیشیم. Its excellent formability, weldability کو, and workability, makes it ideal for marine, آٹوموٹو, فوڈ پروسیسنگ, and general sheet metal work, including tanks, نشانیاں, and cookware. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 اور 5052 lies in their magnesium (مگرا) content, which directly influences strength, as shown in the following comparison:
| Element | 5005 مصر دات | 5052 مصر دات | Key Difference Analysis |
| ایلومینیم (امام) | بقیہ | بقیہ | Base metal for both alloys. |
| میگنیشیم (مگرا) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| کرومیم (بنائیں ایک ب ح) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| مینگنیج (MN) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| سلیکن (اور) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| تانبا (ساتھ) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| زنک (ذ ن) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| آئرن (فے) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(C), اور 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
جے آئی ایس: 5005 corresponds to A5005, اور 5052 کرنے A5052.
-
GB (چین): Both are standardized in China (e.g., GB/T 3880 for sheets)
Mechanical properties of 5005 ایلومینیم شیٹ
| غصہ | Tensile طاقت (N/mm²) | پیداوار طاقت (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 ملی میٹر | 0.8 ملی میٹر | 1.3 ملی میٹر | 2.6ملی میٹر | |||
| اے | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 منٹ | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, ramps, truck beds, and for decorative trim, known for good formability, machinability, and durability in industrial and marine settings.