5005 aluminum sheet is a typical aluminum-magnesium series alloy (5xxx series) known for its medium strength, отличная коррозионная стойкость, and outstanding anodizing surface finish.
5005 сплав aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
РУЙИ / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 мм, as well as plates as thin as 0.2 mm with widths up to 2650 мм, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 Алюминиевый лист Introduction
| Product Name | 5005 Алюминиевый лист |
| Popular Tempers | О, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(B), A95005, 3.3315, AlMg1 |
| 5005 Лист | Толщина: 0.008”–0.24” (0.2mm–6mm), Ширина: 35.4”–104” (900mm–2650mm) |
| 5005 Лист | Толщина: 0.24”–9.84” (6mm–250mm), Ширина: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | Толщина: 0.24”–9.84” (6mm–250mm), Ширина: 35.4”–149.6” (900mm–3800mm) |
| длина | Up to 6 метры; fixed or custom-cut length available |
| Surface Finish | Mill finish, анодированный, brushed, полированный, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & белая пленка, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 Алюминиевый лист
5005 Aluminum sheet with excellent formability, свариваемость, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% магний. Its excellent formability, свариваемость, and workability, makes it ideal for marine, автомобильный, food processing, and general sheet metal work, including tanks, приметы, and cookware. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 а также 5052 lies in their magnesium (Mg) content, which directly influences strength, as shown in the following comparison:
| Element | 5005 сплав | 5052 сплав | Key Difference Analysis |
| алюминий (Al) | Balance | Balance | Base metal for both alloys. |
| магниевый (Mg) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| хром (Cr) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| марганца (Миннесота) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| кремний (и) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| медь (с) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| цинк (Zn) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| Железо (Fe) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(C), а также 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, а также 5052 в A5052.
-
GB (Китай): Both are standardized in China (e.g., ГБ/т 3880 for sheets)
Mechanical properties of 5005 алюминиевый лист
| Характер | Предел прочности (N/mm²) | Предел текучести (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 мм | 0.8 мм | 1.3 мм | 2.6мм | |||
| О | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 min | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, пандусы, truck beds, and for decorative trim, known for good formability, machinability, and durability in industrial and marine settings.