5005 aluminum sheet is a typical aluminum-magnesium series alloy (5xxx series) known for its medium strength, rintangan kakisan yang sangat baik, and outstanding anodizing surface finish.
5005 aloi aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
RUIYI / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 mm, as well as plates as thin as 0.2 mm with widths up to 2650 mm, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 Lembaran aluminium Introduction
| Product Name | 5005 Lembaran aluminium |
| Popular Tempers | yang, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(B), A95005, 3.3315, AlMg1 |
| 5005 Helaian | ketebalan: 0.008”–0.24” (0.2mm–6mm), lebar: 35.4”–104” (900mm–2650mm) |
| 5005 Helaian | ketebalan: 0.24”–9.84” (6mm–250mm), lebar: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | ketebalan: 0.24”–9.84” (6mm–250mm), lebar: 35.4”–149.6” (900mm–3800mm) |
| Negara | Up to 6 meter; fixed or custom-cut length available |
| Surface Finish | Kemasan kilang, anodized, disikat, digilap, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & filem putih, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 Lembaran aluminium
5005 Aluminum sheet with excellent formability, kebolehkimpalan, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% magnesium. Its excellent formability, kebolehkimpalan, dan kebolehkerjaan, makes it ideal for marine, automotif, food processing, dan kerja logam lembaran am, including tanks, tanda-tanda, and cookware. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 dan 5052 lies in their magnesium (mg) content, which directly influences strength, as shown in the following comparison:
| Element | 5005 aloi | 5052 aloi | Key Difference Analysis |
| aluminium (Al) | Balance | Balance | Base metal for both alloys. |
| magnesium (mg) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| Chromium (Cr) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| mangan (Mn) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| Silicon (dan) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| tembaga (dengan) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| zink (Zn) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| besi (Fe) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(C), dan 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, dan 5052 kepada A5052.
-
GB (China): Both are standardized in China (e.g., GB / T 3880 for sheets)
Mechanical properties of 5005 lembaran aluminium
| Temper | Kekuatan tegangan (N/mm²) | hasil kekuatan (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 mm | 0.8 mm | 1.3 mm | 2.6mm | |||
| yang | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 min | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, tanjakan, truck beds, and for decorative trim, known for good formability, machinability, and durability in industrial and marine settings.