5005 aluminum sheet is a typical aluminum-magnesium series alloy (5xxx series) known for its medium strength, 우수한 내식성, and outstanding anodizing surface finish.
5005 합금 aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
루이이 / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 mm, as well as plates as thin as 0.2 mm with widths up to 2650 mm, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 알루미늄 시트 Introduction
| 상품명 | 5005 알루미늄 시트 |
| Popular Tempers | 영형, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(B), A95005, 3.3315, AlMg1 |
| 5005 Sheet | 두께: 0.008”–0.24” (0.2mm–6mm), 폭: 35.4”–104” (900mm–2650mm) |
| 5005 Sheet | 두께: 0.24”–9.84” (6mm–250mm), 폭: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | 두께: 0.24”–9.84” (6mm–250mm), 폭: 35.4”–149.6” (900mm–3800mm) |
| 길이 | Up to 6 meters; fixed or custom-cut length available |
| Surface Finish | 독특한 디자인과 높은 미끄럼 저항을 가진 체크 무늬 플레이트/트레드 알루미늄 시트는 클라이언트의 요구 사항에 따라 다양한 디자인과 패턴으로 쉽게 구성할 수 있습니다., 양극, 닦은, 우아한, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & 흰색 필름, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 알루미늄 시트
5005 Aluminum sheet with excellent formability, 용접성, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% 마그네슘. Its excellent formability, 용접성, 및 작업성, makes it ideal for marine, 자동차의, food processing, 냉간 압연 알루미늄 코일 시트, including tanks, 표지판, and cookware. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 과 5052 lies in their magnesium (마그네슘) content, which directly influences strength, as shown in the following comparison:
| Element | 5005 합금 | 5052 합금 | Key Difference Analysis |
| 알류미늄 (알) | 균형 | 균형 | Base metal for both alloys. |
| 마그네슘 (마그네슘) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| 크롬 (CR) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| 망간 (망간) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| 규소 (과) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| 구리 (와) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| 아연 (아연) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| 철 (철) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(C), 과 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, 과 5052 에 A5052.
-
GB (중국): Both are standardized in China (e.g., GB / T 3880 for sheets)
Mechanical properties of 5005 알루미늄 시트
| 기질 | 인장 강도 (N/mm²) | 항복 강도 (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 mm | 0.8 mm | 1.3 mm | 2.6mm | |||
| 영형 | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 min | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, 경사로, truck beds, and for decorative trim, known for good formability, 가공성, and durability in industrial and marine settings.