5005 aluminum sheet is a typical aluminum-magnesium series alloy (5xxx series) known for its medium strength, 優れた耐食性, and outstanding anodizing surface finish.
5005 合金 aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
ルイイー / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 ミリメートル, as well as plates as thin as 0.2 mm with widths up to 2650 ミリメートル, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 アルミシート Introduction
| 商品名 | 5005 アルミシート |
| Popular Tempers | ザ・, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(B), A95005, 3.3315, AlMg1 |
| 5005 シート | 厚さ: 0.008”–0.24” (0.2mm–6mm), 幅: 35.4”–104” (900mm–2650mm) |
| 5005 シート | 厚さ: 0.24”–9.84” (6mm–250mm), 幅: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | 厚さ: 0.24”–9.84” (6mm–250mm), 幅: 35.4”–149.6” (900mm–3800mm) |
| 長さ | Up to 6 メートル; fixed or custom-cut length available |
| Surface Finish | Mill finish, アルマイト, brushed, 研磨, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & 白フィルム, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTMB209, EN 573, EN 485 |
5005 アルミシート
5005 Aluminum sheet with excellent formability, 溶接性, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% マグネシウム. Its excellent formability, 溶接性, と作業性, makes it ideal for marine, 自動車, food processing, その他板金作業全般, including tanks, サイン, and cookware. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 そして 5052 lies in their magnesium (マグネシウム) content, which directly influences strength, as shown in the following comparison:
| 要素 | 5005 合金 | 5052 合金 | Key Difference Analysis |
| アルミニウム (アル) | Balance | Balance | Base metal for both alloys. |
| マグネシウム (マグネシウム) | 0.5% 〜 1.1% | 2.2% 〜 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| クロム (クロム) | ≤ 0.10% | 0.15% 〜 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| マンガン (マンガン) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| シリコン (と) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| 銅 (とともに) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| 亜鉛 (亜鉛) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| 鉄 (鉄) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(C), そして 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, そして 5052 に A5052.
-
GB (中国): Both are standardized in China (e.g., GB / T 3880 for sheets)
Mechanical properties of 5005 アルミシート
| 気性 | 抗張力 (N/mm²) | 降伏強度 (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 ミリメートル | 0.8 ミリメートル | 1.3 ミリメートル | 2.6ミリメートル | |||
| ザ・ | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 分 | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, ramps, truck beds, and for decorative trim, known for good formability, 被削性, and durability in industrial and marine settings.