5005 יריעת אלומיניום היא סגסוגת טיפוסית מסדרת אלומיניום-מגנזיום (5סדרת xxx) ידוע בחוזק הבינוני שלו, התנגדות קורוזיה מעולה, וגימור משטח אילגון יוצא מן הכלל.
5005 סַגסוֹגֶת aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
RUIYI / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 מ"מ, as well as plates as thin as 0.2 mm with widths up to 2650 מ"מ, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 גיליון אלומיניום Introduction
| שם המוצר | 5005 גיליון אלומיניום |
| Popular Tempers | O, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(ב), A95005, 3.3315, AlMg1 |
| 5005 גיליון | עוֹבִי: 0.008”–0.24” (0.2mm–6mm), רוֹחַב: 35.4”–104” (900mm–2650mm) |
| 5005 גיליון | עוֹבִי: 0.24”–9.84” (6mm–250mm), רוֹחַב: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | עוֹבִי: 0.24”–9.84” (6mm–250mm), רוֹחַב: 35.4”–149.6” (900mm–3800mm) |
| אורך | Up to 6 meters; fixed or custom-cut length available |
| Surface Finish | גימור מיל, אנודייז, מוברש, מְלוּטָשׁ, sandblasted, etched, bright, מרקם |
| Laminated Options | Blue film, clear film, black & סרט לבן, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 גיליון אלומיניום
5005 Aluminum sheet with excellent formability, רְתִיכוּת, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% מגנזיום. Its excellent formability, רְתִיכוּת, ויכולת עבודה, makes it ideal for marine, רכב, food processing, and general sheet metal work, including tanks, שלטים, וכלי בישול. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 ו 5052 lies in their magnesium (mg) content, which directly influences strength, as shown in the following comparison:
| אֵלֵמֶנט | 5005 סַגסוֹגֶת | 5052 סַגסוֹגֶת | Key Difference Analysis |
| אלומיניום (אל) | לְאַזֵן | לְאַזֵן | Base metal for both alloys. |
| מגנזיום (mg) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| כרום (Cr) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| מנגן (Mn) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| הסיליקון (ו) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| נחושת (עם) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| אבץ (Zn) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| מגהץ (Fe) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(ג), ו 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, ו 5052 ל A5052.
-
GB (סין): Both are standardized in China (e.g., GB / T 3880 for sheets)
תכונות מכניות של 5005 גיליון אלומיניום
| מזג | חוזק מתיחה (N/mm²) | כוח התשואה (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 מ"מ | 0.8 מ"מ | 1.3 מ"מ | 2.6מ"מ | |||
| O | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 min | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, רמפות, truck beds, and for decorative trim, known for good formability, יכולת עיבוד, and durability in industrial and marine settings.