5005 aluminum sheet is a typical aluminum-magnesium series alloy (5xxx series) known for its medium strength, مقاومت به خوردگی عالی, and outstanding anodizing surface finish.
5005 آلیاژ aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
RUIYI / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 میلی متر, as well as plates as thin as 0.2 mm with widths up to 2650 میلی متر, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 ورق آلومینیوم Introduction
| نام محصول | 5005 ورق آلومینیوم |
| Popular Tempers | O, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(ب), A95005, 3.3315, AlMg1 |
| 5005 ورق | ضخامت: 0.008”–0.24” (0.2mm–6mm), عرض: 35.4”–104” (900mm–2650mm) |
| 5005 ورق | ضخامت: 0.24”–9.84” (6mm–250mm), عرض: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | ضخامت: 0.24”–9.84” (6mm–250mm), عرض: 35.4”–149.6” (900mm–3800mm) |
| طول | Up to 6 متر; fixed or custom-cut length available |
| Surface Finish | Mill finish, آنودایز, brushed, جلا, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & فیلم سفید, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 ورق آلومینیوم
5005 Aluminum sheet with excellent formability, جوش پذیری, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% منیزیم. Its excellent formability, جوش پذیری, and workability, makes it ideal for marine, خودرو, food processing, and general sheet metal work, including tanks, نشانه, و ظروف آشپزی. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 و 5052 lies in their magnesium (میلی گرم) content, which directly influences strength, as shown in the following comparison:
| Element | 5005 آلیاژ | 5052 آلیاژ | Key Difference Analysis |
| آلومینیوم (آل) | تعادل | تعادل | Base metal for both alloys. |
| منیزیم (میلی گرم) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| کروم (کروم) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| منگنز (منگنز) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| سیلیکون (و) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| فلز مس (با) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| فلز روی (روی) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| اهن (آهن) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(سی), و 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, و 5052 به A5052.
-
گیگابایت (چین): Both are standardized in China (e.g., GB/T 3880 for sheets)
خصوصیات مکانیکی 5005 ورق آلومینیوم
| خوی | استحکام کششی (N/mm²) | قدرت عملکرد (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 میلی متر | 0.8 میلی متر | 1.3 میلی متر | 2.6میلی متر | |||
| O | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 min | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, ramps, truck beds, and for decorative trim, known for good formability, ماشین کاری, and durability in industrial and marine settings.