5005 aluminum sheet is a typical aluminum-magnesium series alloy (5سلسلة الثلاثون) known for its medium strength, مقاومة ممتازة للتآكل, and outstanding anodizing surface finish.
5005 أشابة aluminum sheet is a non-heat treatable rolled product supplied as either plate or coil and is the softest of the 5000 series alloys making this alloy very suitable for forming and welding. It has excellent corrosion resistance properties and is suitable for a broad range of applications.
روي / RAYIWELL offers aluminum plates with a maximum width of up to 3800 mm and a maximum thickness of 250 مم, as well as plates as thin as 0.2 mm with widths up to 2650 مم, meeting a wide range of thickness and width requirements for various orders.
UNS A95005 ورقة الألمنيوم Introduction
| اسم المنتج | 5005 ورقة الألمنيوم |
| Popular Tempers | ال, H14, H24, H32, H34, H36, H38 |
| Equivalent Names | AW-5005, AlMg1(ب), A95005, 3.3315, AlMg1 |
| 5005 ورقة | سماكة: 0.008”–0.24” (0.2mm–6mm), عرض: 35.4”–104” (900mm–2650mm) |
| 5005 ورقة | سماكة: 0.24”–9.84” (6mm–250mm), عرض: 35.4”–104” (900mm–2650mm) |
| 5005 Extra Wide | سماكة: 0.24”–9.84” (6mm–250mm), عرض: 35.4”–149.6” (900mm–3800mm) |
| الطول | Up to 6 متر; fixed or custom-cut length available |
| Surface Finish | Mill finish, بأكسيد, نحى, مصقول, sandblasted, etched, bright, textured |
| Laminated Options | Blue film, clear film, black & فيلم أبيض, paper (Film thickness: 50μm / 80μm) |
| Standards | ASTM B209, EN 573, EN 485 |
5005 ورقة الألمنيوم
5005 Aluminum sheet with excellent formability, حام, and anodising properties. 5052 Aluminium is A marine-grade alloy with higher strength and corrosion resistance, particularly suited for marine and automotive applications.
5052 aluminum sheet is a popular, corrosion-resistant alloy with 2.5% المغنيسيوم. Its excellent formability, حام, وقابلية العمل, makes it ideal for marine, السيارات, معالجة الغذاء, وأعمال الصفائح المعدنية العامة, including tanks, علامات, وأدوات الطهي. It’s a non-heat-treatable alloy, often supplied in tempers like H32, offering good strength and bright finish suitable for painting or anodizing, though it’s not easily machined.
The primary difference between 5005 و 5052 lies in their magnesium (ملغ) content, which directly influences strength, as shown in the following comparison:
| عنصر | 5005 أشابة | 5052 أشابة | Key Difference Analysis |
| الألومنيوم (شركة) | Balance | Balance | Base metal for both alloys. |
| المغنيسيوم (ملغ) | 0.5% ~ 1.1% | 2.2% ~ 2.8% | The most critical difference. 5052’s higher Mg content gives it significantly higher strength. |
| الكروم (كر) | ≤ 0.10% | 0.15% ~ 0.35% | 5052 contains more Cr, enhancing its stress corrosion resistance. |
| المنغنيز (Mn) | ≤ 0.20% | ≤ 0.10% | Slightly higher limit in 5005. |
| السيليكون (و) | ≤ 0.30% | ≤ 0.25% | Similar low levels in both. |
| نحاس (مع) | ≤ 0.20% | ≤ 0.10% | Lower in 5052, beneficial for corrosion resistance. |
| زنك (الزنك) | ≤ 0.25% | ≤ 0.10% | Lower in 5052. |
| حديد (Fe) | ≤ 0.70% | ≤ 0.40% | Lower impurity limit in 5052. |
These alloys are specified in major international standards systems.
-
ISO/DIN: 5005 is known as AlMg1(C), و 5052 is similar to AlMg2.5.
-
ASTM/ASM: 5052 is a standard ASTM alloy. Both are covered by standards like ASTM B209.
-
JIS: 5005 corresponds to A5005, و 5052 إلى A5052.
-
GB (الصين): Both are standardized in China (على سبيل المثال, غب / ت 3880 for sheets)
الخواص الميكانيكية 5005 ورقة الألمنيوم
| لين، لطف، هدأ | قوة الشد (N/mm²) | قوة العائد (N/mm²) | Elongation on 50mm (%) | |||
| 0.5 مم | 0.8 مم | 1.3 مم | 2.6مم | |||
| ال | 95-145 | 35 | 18 | 20 | 21 | 22 |
| H12 | 125-170 | 80 | 4 | 5 | 6 | 8 |
| H14 | 145-185 | 100 | 3 | 3 | 5 | 6 |
| H18 | 185 دقيقة | 165 | 1 | 2 | 3 | 3 |
5052-H32 aluminum checkered plate is a strong, corrosion-resistant aluminum alloy (5052) in a semi-hardened temper (H32) with a raised diamond or tread pattern, used for anti-slip surfaces on walkways, ramps, truck beds, and for decorative trim, known for good formability, امكانيه, and durability in industrial and marine settings.